Abstract
Ionic transport in concrete can be described using the formation factor, which is the ratio of the resistivity of the concrete and the pore solution resistivity. The pore solution resistivity may be assumed, directly measured, or computed from the pore solution composition. This paper describes an experimental investigation aimed at determining the feasibility of using X-ray fluorescence (XRF) to obtain the alkali concentrations of the pore solution which enable the calculation of pore solution resistivity. In order to do this, simulated pore solutions containing known amounts of sodium and potassium were prepared and analyzed using XRF. XRF was performed on two sample types: (1) the simulated solutions and (2) beads where the water from the solution is evaporated and the remaining material is fused using a fluxing agent. The compositions obtained experimentally from XRF are compared to known compositions to demonstrate the accuracy of the technique. In addition, the measured simulated pore solution resistivity was compared to the simulated pore solution resistivity calculated from XRF measurements. The results indicate that the composition had an average error of 0.50% while the estimated simulated pore solution resistivity had an average error of 10.95%. The results of this study indicate that XRF has the potential to be an alternative to the time consuming methods currently used to measure the composition of the pore solution.